简介:Fe3AlandCr18-Ni8steelwerebondedinvacuumandaninterfacewasformedbetweenFe3AlandCr18-Ni8steel.Stressdistributionatthediffusion-bondedinterfacewasresearchedbynumericalsimulationandfiniteelementmethod(FEM).TheresultsindicatedthatthepeakstressappearedattheinterfacenearCr18-Ni8steelside.Thisisthekeyfactortoinducecrackatthisposition.Withtheenhancementofheatingtemperature,thepeakstressatthebondedinterfaceincreases.Whenthetemperatureis1100℃,thepeakstressisupto65.9MPa,whichisbiggerthanthatat1000℃by9.4%.Inaddition,thepeakstressbecomesbiggerwiththeincreaseofthethicknessofbasemetalfrom1mmto8mm.Whilethethicknessismorethan8mm,thepeakstressvariesslightlywiththechangeofthethickness.
简介:ESD(electrosparkdeposition)isapromisingprocesstoproducehardandwear-resistingcoatingsonmetallicsubstrates.InthispapermicrostructureandinterfacialcharacteristicsoftheWC92-Co8coatedontitaniumandcarbonsteelarepresented.Ametallurgicalbondingbetweenthecoatingandsubstrateisobtained.TheTielementwasfoundtodistributeinWC92-Co8atthemetalpool,aswellastheinterfacebydiffusion.SomenewphaseswereproducedinthecoatinglayerduetothechemicalreactionduringtheESDprocess.ExperimentalobservationandthermodynamicanalysiswereutilizedtostudythemechanismofESD.
简介:TiC/Cr18Ni8steelbondedcarbidesweresynthesizedbyvacuumsinteringwithmixedpowdersofiron,ferrotitanium,ferrochromium,colloidalgraphiteandnickelasrawmaterials.Themicrostructureandmicrohardnessofthesteelbondedcarbideswereanalyzedbyscanningelectronmicroscope(SEM),X-raydiffraction(XRD)andRockwellhardometer.ResultsshowthatthephasesofsteelbondedcarbidesmainlyconsistofTiCandFe-Cr-Nisolidsolution.ThesynthesizedTiCparticlesarefine.Mostofthemarenotmorethan1μm.Withtheincreaseofsinteringtemperature,theporosityofTiC/Cr18Ni8steelbondedcarbidesdecreasesandthedensityandhardnessincrease,butthesizeofTiCparticlesslightlyincreases.Underthesamesinteringconditions,thedensityandhardnessofsteelbondedcarbideswithC/Tiatomicratio0.9arehigherthanthosewithC/Tiatomicratio1.0.TheTiCparticleswithC/Tiatomicratio0.9aremuchfinerandmorehomogeneous.
简介:Thefatiguepropertiesoffrictionstirwelded(FSW)buttjointandbasemetalofMB8magnesiumalloywereinvestigated.ThecomparativefatiguetestswerecarriedoutusingEHF-EM200K2-070-1AfatiguetestingmachineforbothFSWbuttjointandbasemetalspecimens.ThefatiguefractureswereobservedandanalyzedusingascanningelectronmicroscopeofJSM-6063LAtype.TheexperimentalresultsshowthatthefatigueperformanceoftheFSWbuttjointofMB8magnesiumalloyissharplydecreased.Theconditionalfatiguelimit(2×10~6)ofbasemetalandweldedbuttjointisabout77.44MPaand49.91MPa,respectively.Theconditionalfatiguelimit(2×10~6)oftheweldedbuttjointis64.45%ofthatofbasemetal.Themainreasonsarethattheweldingcanleadtostressconcentrationintheflasharea,tensileweldingresidualstressintheweldedjoint(Theresidualstressvaluewas30.5MPa),aswellasthegrainsizeisnotuniformintheheat-affectedzone.Thecleavagestepsorquasi-cleavagepatternspresentonthefatiguefracturesurface,thefracturetypeoftheFSWbuttjointbelongstoabrittlefracture.