简介：(Cu60Zr30Ti10)98Y2bulkmetallicglass(Φ4mm×70mm)wasobtainedsuccessfullybycoppermouldcoolingandspraying-casting,andsomesampleswereisothermallyannealedattemperaturesof473and623K,whichwaslowerthantheglasstransitiontemperature(Tg)for1h.Microstructureandpropertiesofas-castandannealedsampleswerestudied.Crystallizationphases(Cu10Zr7andCuZr)wereobservedinannealedsamples,andthespeciesandfractionofthesephasesincreasedwithincreasingannealingtemperature.Mic...

简介：采用超音速等离子喷涂法在1045钢表面制备NiCr-Cr3C2涂层，分析涂层的微观结构及化学成分以及涂层的晶粒结构，利用MICROMET-6030显微硬度仪和Nano-test600纳米压痕仪测定涂层的显微硬度与弹性模量，通过油润滑微动摩擦磨损试验测试涂层的微动磨损性能。结果表明，NiCr-Cr3C2涂层为明显的层状结构，具有单晶、纳米多晶与过渡区共存的复杂晶体学结构，显微硬度HV0.3高达998，约为基体材料硬度的3倍，弹性模量为224.6GPa；涂层的微动摩擦因数随载荷增大而减小，随温度升高而增大。喷涂层的抗微动摩擦磨损性能较基体优异，摩擦因数及体积磨损量分别比基体降低36.7%和55.6%。涂层的磨损机理以磨粒磨损和疲劳剥落为主。

简介：采用压力烧结法制备不同碳含量的WC-10Co-0.6Cr3C2硬质合金，通过金相组织观察、硬度测试、比饱和磁化强度和矫顽磁力的分析，研究该合金的微观组织结构和性能。结果表明，随碳含量增加，合金的饱和磁化强度增大，而密度、矫顽磁力及硬度均降低；在压力烧结条件下，对于WC-10Co-0.6Cr3C2合金，两相正常组织对应的碳含量范围为5.41%～5.55%。碳含量低于5.41%时出现缺碳相η相，碳含量高于5.55%时出现石墨相。

简介：通过电化学分析与测试，研究B4C体积分数分别为20%、30%、40%的B4C/Al基复合材料及其基体合金（6061铝合金）在不同浓度及不同温度的硫酸溶液中的腐蚀行为。由动态极化曲线和阻抗谱得到相应的电化学参数，并利用阻抗分析软件对该复合材料和基体合金腐蚀过程的等效电路进行模拟，分析腐蚀机理，通过Arrhenius方程计算腐蚀过程中B4C/Al基复合材料与6061铝合金的反应活化能，并分析两者的焓变与熵变，对腐蚀前后2种材料界面的微观结构进行观察。结果表明：B4C/Al基复合材料在硫酸溶液中的腐蚀速率随B4C颗粒含量增加而增大，基体铝合金在硫酸中的耐腐蚀性能高于B4C/Al基复合材料。B4C/Al基复合材料和基体铝合金在硫酸中的腐蚀速率都随硫酸溶液浓度增加而增大；当溶液温度升高时，二者的腐蚀速率都快速增加。B4C/Al基复合材料和Al基体合金在硫酸溶液中的腐蚀都表现为明显的点蚀。铝基体材料在硫酸溶液中的反应活化能大于B4C/Al基复合材料，计算所得活化焓与活化熵的值均表明复合材料的腐蚀反应比基体合金更容易进行，因而遭受腐蚀更严重。

简介：

简介：采用化学镀法对TiH2粉末表面镀Ni,制备Ni/TiH2复合粉末。通过X射线衍射（XRD）、扫描电镜（SEM）、能谱分析（EDS）及差热分析（DSC/TG）对Ni/TiH2复合粉末进行表征,探索Ni镀层的生长及作用机理,建立镀层在粉末表面的生长模型。结果表明：施镀温度为85℃时Ni/TiH2复合粉末表面Ni层包覆完整,镀层均匀致密,Ni层厚度约为1.0~2.0μm;施镀温度低于65℃时施镀几乎无法进行,而施镀温度高于95℃时,镀层很不均匀,且容易脱落;镀层的生长机制遵循奥斯特瓦尔德（Ostwaldripening）机制;与包覆前TiH2粉末相比,Ni/TiH2复合粉末的释氢反应开始温度由450℃上升至540℃。包覆层可降低TiH2粉末和熔融铝的温度梯度,从而推迟开始释氢的时间。

简介：采用选择性激光熔覆法,在基板温度分别为100,150,和200℃条件下制备M2粉末高速钢合金,分析基板温度对合金组织结构与力学性能的影响。结果表明,基板温度升高有利于提高M2粉末高速钢的致密度和整体组织的均匀性。当基板温度为200℃时,高速钢组织均匀致密,各元素固溶程度高,且碳化物含量高,组织中柱状晶不再沿Z轴方向单一生长,同时合金的显微硬度(HV0.1)达到最高,HV0.1为1150,相比基板温度为100℃时的合金提高近40%。随基板温度从100℃升高到200℃,沿Z轴打印的M2高速钢室温抗拉强度从865.23MPa降低到443.85MPa,主要原因是合金中单一方向的柱状晶数量减少。

简介：

简介：以Nb2O5、In（NO3）3和Sm（NO3）3为原料,采用溶胶-凝胶法制备新型光催化材料Sm2InNbO7。采用X射线衍射（XRD）、扫描电镜（SEM）、比表面积分析（BET）以及紫外-可见漫反射光谱（UV-Visdiffusereflectancespectroscopy）技术对该材料的结构、形貌和光吸收性能进行表征。以可见光下亚甲基蓝（MB）的脱色降解为模型反应,考察煅烧温度、催化剂用量、H2O2用量和pH值对Sm2InNbO7光催化性能的影响。结果表明,煅烧温度为700℃时即可获得具有烧绿石结构的Sm2InNbO7。随焙烧温度升高,催化剂结晶度增加,粒径增大,比表面积下降,吸收边界出现一定的蓝移;在850℃下煅烧3h获得的Sm2InNbO7样品具有最高的催化活性,当50mL质量浓度的10mg/L的MB溶液中催化剂用量为0.1g、30%H2O2溶液用量为0.5mL、pH=6时,亚甲基蓝的降解率高达93.8%,明显优于固相法制备的Sm2InNbO7以及P-25TiO2。较高的pH值有利于光催化反应的进行。

简介：本文介绍了应用“汽液两相流”自调节液位控制装置及ＳＸＹ系列液位显示器对２＃汽轮发电机高加进行改造的可能性及效果。

简介：

简介：

简介：一系列立方的稀土元素sesquioxidesRE2O3的拉曼系列(RE=Eu，Gd，Dy，惊讶，嗯，Tm，Yb，陆，Sc和Y)被拉曼光谱学与532和785根nm激光线调查。丰富的另外的乐队由于激光激动的光被观察。为Eu2O3，Dy2O3，Ho2O3，Er2O3，Tm2O3和Yb2O3，，光主要为Gd2O3，Lu2O3，Sc2O3和Y2O3来自内在的三价的lanthanide离子，他们的光被归因于象Eu3+，Nd3+和Er3+那样的另外的光lanthanide离子的踪迹杂质。这调查为检测踪迹作为一个有用工具证实了拉曼光谱学光lanthanide杂质。

简介：265m^2烧结机主传动装置的驱动电机与三环减速机集成为一套一次减速驱动装置部件,整体悬挂于二次减速机高速轴上,驱动电机通过三环减速机带动二次减速机实现对烧结机星轮主轴的回转驱动。从2012年至今,三环减速机出现不同程度的损坏。本文主要对三环减速机损坏的原因进行分析,利用修复工艺将其恢复到正常生产使用条件。

简介：

简介：ThephaseandmorphologytransformationduringthehydrothermaltreatingprocessofY2O3wasevaluatedwithX-raydiffcrcnce(XRD),scanningelectronmicroscopy(SEM),transmissionelectronmicroscopy(TEM),particlesizeandspecificsurfaceareadetermination.TheresultsshowedthatthecubicY2O3didnottransferintohexagonalY(OH)3inpurewater.Therefore,purehexagonalY(OH)3withnanotubeandmicrorodmorphologieswereobtainedbyhydrothermaltreatingY2O3at150℃for12hin15mlof2mol/LNaOHsolutionwithandwith-outPVAorPEGItwassuggestedthatthecharacteristicpreferentialgrowthofY(OH)3wasattributedtothestructureanisotropyofhexahedronY(OH)3.TheadditionofPVAorPEGcouldpromotetheformingprocessofnanotubesbyselectiveadsorptionondifferentcrystalplanes,whichalteredthegrowthratealongdifferentdirectionsandresultedinthediffusionlimitofconstructingionsinthecentertopofrods.Finally,Y(OH)3:EuandY2O3:Eunanotubeswerealsosynthesizedbyusingthismethod,andtheirphotoluminescencepropertieswereevaluated.

简介：MeltspinningtechnologywasusedtopreparetheMg2Ni-type(Mg24Ni10Cu2)100–xNdx(x=0,5,10,15,20)alloysinordertoobtainananocrystallineandamorphousstructure.TheeffectsofNdcontentandspinningrateonthestructuresandelectrochemicalhydrogenstorageperformancesofthealloyswereinvestigated.ThestructurecharacterizationsofX-raydiffraction(XRD),transmissionelectronmicroscopy(TEM)andscanningelectronmicroscopy(SEM)linkedwithenergydispersivespectroscopy(EDS)revealedthattheas-spunNd-freealloydisplayedanentirenanocrystallinestructure,whereastheas-spunNd-addedalloysheldananocrystallineandamorphousstructureandthedegreeofamorphizationvisiblyincreasedwiththerisingofNdcontentandspinningrate,suggestingthattheadditionofNdfacilitatedtheglassformingoftheMg2Ni-typealloy.TheelectrochemicalmeasurementsindicatedthattheadditionofNdandmeltspinningimprovedtheelectrochemicalhydrogenstorageperformancesofthealloyssignificantly.Thedischargecapacitiesoftheas-castandspunalloysexhibitedmaximumvalueswhenNdcontentwasx=10,whichwere86.4,200.5,266.3,402.5and452.8mAh/gcorrespondingtothespinningrateof0(As-castwasdefinedasthespinningrateof0m/s),10,20,30and40m/s,respectively.Thecyclestability(S20,thecapacitymaintainrateat20thcycle)oftheas-castalloyalwaysrosewiththeincreasingofNdcontent,andthoseoftheas-spunalloysexhibitedthemaximumvaluesforNdcontentx=10,whichwere77.9%,83.4%89.2%and89.7%,correspondingtothespinningrateof10,20,30and40m/s,respectively.

简介：用溶胶-凝胶法制备镍锌共掺杂Z型锶钴铁氧体Sr3（NiZn）xCo2（1-x）Fe24O41（x=0～0.5）粉末。用X射线衍射（XRD）和扫描电镜（SEM）表征该铁氧体粉末的晶体结构和表面形貌，并测试其室温磁滞回线和室温电阻率。用微波矢量网络分析仪测定该粉末在2～18GHz微波频率范围的复介电常数和复磁导率，根据测量数据计算电磁损耗角正切及微波反射率，分析该材料的微波吸收性能与电磁损耗机理。结果表明：Sr3（NiZn）xCo2（1-x）Fe24O41粉末呈六角片状形貌，晶体结构为Z型，具有良好的软磁特性；x=0.3时该材料的电阻率最低，微波吸收效果最好，在13.5GHz频率的吸收峰为25.1dB，10dB频带宽度为7.7GHz，兼具强的磁损耗和弱的介电损耗。

简介：采用浓HNO3/浓H2SO4混合酸在60℃超声环境下对T300碳纤维进行表面氧化处理，并以其为增强体制备碳纤维/环氧树脂复合材料。利用X射线光电子能谱仪、拉曼光谱仪、扫描电镜、原子力显微镜对表面氧化前后的碳纤维形态与表面化学性质进行表征，研究氧化时间对纤维的表面形貌与表面性质以及碳纤维/环氧树脂基复合材料力学性能的影响。结果表明，氧化初期，碳纤维表面生成S—、N—含氧基团，以及—OH和—C=O；后期形成—COOH，氧化时间为15min时，—COOH的浓度达到最大值。碳纤维/环氧树脂复合材料的强度随混合酸氧化时间延长而不断增强，氧化15min时强度达到峰值，相比于未氧化处理的样品，复合材料层剪切强度从16.3MPa提高到38.8MPa，抗弯强度从148.3MPa提高到379.7MPa。