简介：分析了模具失效原因,结合工厂实际条件,因地制宜,对3Cr2W8V钢进行渗碳处理,提高了模具使用寿命,增加了工厂的经济效益.

简介：TiO2nanoparticleswithdifferentphasesarepreparedbyhydrolysisoftitaniumtetrabutoxideinthepresenceofHCl.ThecompositionandmicrostructureoftheresultingsamplesarestudiedbyXRDandTEM.TheseresultsshowthattherangeofparticlesizeofTiO2isfrom20to30nm.ThemechanismofTiO2photocatalysisreactionhasbeendiscussedextensively.PhotocatalyticactivitiesofnanometerTiO2arealsoevaluatedbydegradationofthecrystalvioletsolution.ExperimentalresultsindicatethatthesynergisticactionofH2O2andultrasonicwavegreatlyenhancesphoto-catalyticreactionofTiO2.

简介：TheeffectofyttriaonthesolidreactionmechanismofaCaHPO4·2H2O+CaCO3systematdifferenttemperatureswasexperimentallystud-ied.Thesampleswithandwithoutyttriaweresubjectedtothermogravimetric/differentialscanningcalorimetrymeasurement.ThesampleswereheattreatedatthetemperaturescorrespondingtothepeaksontheDSCspectra,andtheresultedphasecompositionswereidentifiedbyX-raydiffraction.Thetransformationmechanismwasdeducedbycomparingthephasesobtainedatdifferenttemperatures.Theresultsshowthatthetransformationsatbelow1073Karenotaffectedbyyttria,butallthoseatabove1073Karecompletelyaltered.Theformationtem-peratureofhydroxyapatitedecreasesby134K,andthedecompositiontemperatureincreasesby38K.ThepolymorphoustransformationofCa3(PO4)2fromβphasetoαphaseincreasesby47K.Thethermodynamicpropertiesofthetransformationsatabove1073Karealsomodi-fiedbytheadditionofyttria;thatis,theendothermalpeaksaresubstitutedbyexothermalpeaks.

简介：激光冲击强化是一种新型表面处理技术,利用高功率激光束冲击金属零件表面,在零件表面形成较大的残余压应力,可有效改善零件的疲劳性能。以发动机1Cr11Ni2W2MoV叶片为研究对象,对其进行了激光冲击强化处理,研究强化处理对材料的微观组织和疲劳性能的影响。研究结果表明：相比未处理试样,激光冲击强化在1Cr11Ni2W2MoV叶片材料表层形成较大的残余压应力,表层晶粒更为细化,叶片的疲劳寿命提高1.7倍。

简介：ThermodynamicmodelsofcalculatingmassactionconcentrationsforstructuralunitsorioncouplesinRbCl-H2ObinaryandRbCl-RbNO3-H2Oternarystrongelectrolyteaqueoussolutionsweredevelopedbasedontheionandmoleculecoexistencetheoryat298.15K.Atransformationcoefficientisneededtocomparethecalculatedmassactionconcentrationandthereportedactivitybecausetheyareobtainedatdifferentstandardstatesandconcentrationunits.TheresultsshowthatthetransformationcoefficientsbetweenthecalculatedmassactionconcentrationsandthereportedactivitiesofthesamestructuralunitsorioncouplesinRbCl-H2ObinaryandRbCl-RbNO3-H2Oternarystrongelectrolyteaqueoussolutionschangeinaverynarrowrange.ThetransformedmassactionconcentrationsofstructuralunitsorioncouplesinRbCl-H2Obinarysystemareingoodagreementwiththereportedactivities.ThetransformedmassactionconcentrationsofRbClandRbNO3inRbCl-RbNO3-H2Oternarysolutionarealsoingoodagreementwiththereportedactivities,aRbCland3RbNOa,withdifferenttotalionicstrengthsas0.01,0.05,0.1,0.5,1.0,1.5,2.0,3.0and3.5mol/kg,respectively.AllthoseresultsmeanthedevelopedthermodynamicmodelofstrongelectrolyteaqueoussolutionscanreflectstructuralcharacteristicsofRbCl-H2ObinaryandRbCl-RbNO3-H2Oternarystrongelectrolyteaqueoussolutionsandthemassactionconcentrationalsostrictlyfollowsthemassactionlaw.

简介：散热问题已成为电子设计者面前的最大挑战之一,研究开发导热性好并且与铜箔（铜线路）间有较好的粘结强度和刚度的绝缘层材料对HDI电路板的应用具有重要意义。随着2008年欧盟RoHS指令的逐步开始实施,现有电子元器件含溴阻燃体系逐渐禁用,因此无卤2W导热率导热膜开发意义重大。

简介：有5-8nm的尺寸的做Eu的GaOOHnanoparticles被热水的方法作为表面活化剂用钠dodecylbenzenesulfonate(SDBS)准备。做Eu的-Ga2O3和-Ga2O3被退火进一步制作GaOOH:Eu然后由X光检查衍射(XRD)描绘了，传播电子显微镜学(TEM)和光致发光(PL)。TEM结果显示出那monodisperse做Eu3+的GaOOHnanoparticles形式然后变换进通过退火的做Eu3+的-Ga2O3和-Ga2O3GaOOH:在600和900点的Eunanoparticles?????????????????@

简介：

简介：采用化学平衡模拟软件GEMS预测了锌湿法冶金过程中涉及的锌在Zn（Ⅱ）-NH3-H2O和Zn（Ⅱ）-NH3-Cl--H2O体系中的溶解度,并构建了其含锌物种分布图和优势区图。采用平衡实验方法测定了相同条件下锌的溶解度,其结果与预测结果相吻合。含锌物种的分布图和优势区图表明,在弱碱性条件下,2个体系均为以锌氨和羟基锌氨配合物为溶液的主要物种,其中Zn（NH3）24-为主要优势物种;在Zn（Ⅱ）-NH3-Cl--H2O体系中,锌氨氯三元配合物的形成能有效增大锌在中性条件下的溶解度,在该体系中存在Zn（OH）2、Zn（OH）1.6Cl0.4和Zn（NH3）2Cl23种固相,固相产物的形成取决于体系中总锌、总氨和总氯浓度。这些热力学平衡图表明了体系中各种物种之间的相互影响作用,并预测了总氨和总氯浓度的变化对锌溶解度的影响,为锌湿法冶金提供了热力学数据。

简介：多层的Nb2O5部nanoporous电影被控制阳极化过程成功地在包含4的乙烯乙二醇在Nb表面上综合?vol%HF并且2?vol%H2O2电解质。nanoporous电影被地排放扫描详细描绘电子显微镜学(FESEM)，传播电子显微镜学(TEM)，和X光检查衍射(XRD)。Nb2O5部nanoporous电影与~的方面墙厚度有多层的形态学5?nm，有~的一条直径的不规则的毛孔25?nm，并且一段多达7.39?m，取决于阳极化时间。为多层的Nb的机制<潜水艇class=“a-plus-plus”>2O<潜水艇class=“a-plus-plus”>5nanoporous形成也被讨论。这些nanoporous材料能在太阳能电池，煤气的传感器，催化剂，光过滤器，和电容器的地里是很有用的。

简介：在H2SO4-Fe2（SO4）3体系中研究载金黄铁矿的浸出动力学,探讨反应温度、Fe3＋浓度、硫酸浓度、搅拌速度等对黄铁矿浸出的影响规律。结果表明：在H2SO4-Fe2（SO4）3体系中,在30~75°C下黄铁矿浸出过程主要受化学反应控制Fe3＋浓度与黄铁矿的浸出呈正相关,通过Arrhenius经验公式求得浸出表观活化能为51.39kJ/mol。EDS与XPS分析结果表明：黄铁矿氧化过程中硫的氧化经一系列中间形态,最终被氧化成硫酸根,并伴有部分元素硫生成,符合硫代硫酸根氧化路径机理。

简介：ThesusceptibilityofweldedjointfortheX65pipelinesteeltoH2Sstresscorrosioncracking(SCC)isinvestigated.SCCtestsonthesteelarecarriedoutintheenvironmentbasedonNACETM-01-77solutionwithsaturatedgaseousH2S.Thethresholdstressintensityfactorandcrackpropagationvelocityarecalculatedaccordingtowedge-openingloading(WOL)specimens.Thethree-dimensionalelastic-plasticfiniteelementanalysisofWOLspecimensisperformedbyusingtheFEMprogrammingpackageANSYS.Stressfieldandconcentrationofhydrogendistributionpropertyaheadofthecracktipareobtained.ThispapersurveyedthemicrostructureofweldedjointandstudiedonthemechanicalpropertiesofX65pipelinesteel.Itprovidesexperimentalbasisforstudyingstresscorrosion.Theresultsofnumericalanalysisareconsistentwithconclusionsofstresscorrosiontest.

简介：钛酸铝系复合材料中钛酸铝的体积分数不同，会导致Al2TiO5／Al2O3复合材料的抗铝液浸渗性能的不同。在Al2TiO5中分别按10％、20％、40％、60％、80％、90％（体积分数）引入Al2O3进行复合。通过对渗铝试样的外观形貌、微观结构分析，进而对其铝液浸渗性能进行了分析比较，发现富钛酸铝的钛酸铝／氧化铝复合材料（妒（AL2TiO5）〉40％）抗铝液浸渗性能好；而富氧化铝的钛酸铝／氧化铝复合材料（φ（Al2TiO5）〈20％）有金属铝液沿热震产生的裂纹渗入复合材料内部，容易导致复合材料断裂失效。该研究结果对可靠应用钛酸铝系复合材料作为铝液的容器具有实际工程应用价值。

简介：Pt(Ⅱ)andPd(Ⅱ)complexeswith2',3',4',5,7-pentahydroxy-flavoneweresynthesizedandcharacterizedbyelementalanalysis,molarconductance,IR,1HNMR,TG-DTA,UV-Visspectroscopictechniques,andfluorescenceanalysis.Thescavengingeffectonthesuperoxideradical(O-2)andtheinhibitoryeffectonlipidperoxideswerealsoinvestigated.Boththeligandandthecomplexesexhibitscavengingeffectonsuperoxideradicals,andtheeffectofthecomplexesisgreaterthanthatoftheligand.ThePt(Ⅱ)complexexhibitsthestrongestscavengingefficiency.BothPt(Ⅱ)andPd(Ⅱ)complexeshavetheinhibitoryeffectonlipidperoxides,andtheeffectofthecomplexesisgreaterthanthatoftheligand,butthePt(Ⅱ)complexhasahigheffectofpromotinglipidperoxides.

简介：MechanicallyactivatedW-Cupowdersweresinteredbyasparkplasmasinteringsystem(SPS)inordertodevelopanewprocessandimprovethepropertiesofthealloy.Propertiessuchasdensityandhardnessweremeasured.ThemicrostructuresofthesinteredW-CualloysampleswereobservedbySEM(scanningelectronmicroscope).Theresultsshowthatsparkplasmasinteringcanobviouslylowerthesinteringtemperatureandincreasethedensityofthealloy.Thisprocesscanalsoimprovethehardnessofthealloy.SPSisaneffectivemethodtoobtainW-Cupowderswithhighdensityandsuperiorphysicalproperties.

简介：为了分析含钒钛转炉渣氧压酸浸过程的热力学特点,根据高温水溶液中计算标准摩尔吉布斯自由能和活度系数的经验公式,通过计算得到了氧分压0.5MPa、对应离子的质量浓度0.1mol/kg、温度60～200℃条件下V-Ti-H2O系的电位-pH图。在pH〈2的酸性条件下,可溶性V3＋,VO2＋,VO2＋的稳定区几乎全部包含在TiO2的稳定区范围内,随着温度由60℃升高到200℃,钒、钛稳定共存区对应的氧化还原电位逐渐增大,pH逐渐降低。钒、钛稳定区的共存特点从热力学角度为转炉渣采用氧压酸浸工艺通过一步酸浸将钒浸出的同时使钛富集在渣中提供了理论依据。含钒钛转炉渣的氧压酸浸实验结果表明,在浸出温度140℃、氧分压0.5MPa、粒度0.055～0.075mm、液固比15：1、浸出时间120min、搅拌速度500r/min、初酸浓度200g/L的条件下,钒的浸出率为96.87%,钛的浸出率为8.76%。钒与钛通过氧压酸浸工艺能够得到有效分离,实验结果与热力学计算结果一致。

简介：Themicrostructuresofas-castandas-solutionMg–12Gd–2Er–1Zn–0.6Zralloyswereinvestigatedbyopticalmicroscopy（OM）,scanningelectronmicroscopy（SEM）,transmissionelectronmicroscopy（TEM）,highresolutiontransmissionelectronmicroscopy（HRTEM）X-raydiffraction（XRD）andselected-areaelectrondiffraction（SAED）inthepresentinvestigation.TheresultsshowthattheprimaryeutecticphaseMg5（Gd,Er,Zn）andsomeflocculentfeaturesarefoundintheas-castalloy;theSAEDpatternindicatesthattheseflocculentfeaturesarethedenseareasofstackingfaults.The14H-LPSOstructureprecipitatesinthetemperaturerangeof673–793K,andthevolumefractionof14H-LPSOstructureincreaseswiththeextensionofheatingtime;however,thereisnoprecipitationof14H-LPSOstructurewhenthetemperaturereachesupto803K.Inaddition,theMg5（Gd,Er,Zn）phasedissolvesgraduallyalongwiththeprecipitationof14H-LPSOstructure.

简介：采用动电位和电化学阻抗谱技术研究了纯Ti（2级）和Ti-Pd合金（7级）的耐腐蚀性能。实验温度为36.6℃,实验溶液包括模拟的健康人体条件的pH7.4的PBS溶液和添加了H2O2（0.015mol/L）的pH5.2的炎症状态的PBS溶液。Ti-Pd合金（7级Ti）,在含H2O2的PBS溶液中,其耐腐蚀性能比纯Ti的好（较低的腐蚀电流密度）,表明其是一种很好的骨科植入材料。

简介：TheslidingfrictionandwearbehaviorsofMg–11Y–5Gd–2Zn–0.5Zr(wt%)alloywereinvestigatedunderoillubricantconditionbypin-on-diskconfigurationwithaconstantslidingdistanceof1,000minthetemperaturerangeof25–200°C.Resultsindicatethatthevolumetricwearratesandaveragefrictioncoefficientsdecreasewiththeincreaseofslidingspeeds,andincreasewiththeincreaseoftesttemperaturebelow150°C.ThehardandthermallystableMg12(Y,Gd)Znphasewithlong-periodstackingorderstructureinthealloypresentssignificantwearresistance.Thewearmechanismbelow100°Cisabrasivewearasaresultofplasticextrusiondeformation.Thecorporateeffectsofsevereabrasive,oxidative,anddelaminatingwearresultinthetribologicalmechanismabove100°C.

简介：某型号飞机电缆装配前进行例行检查时,发现ZG0Cr14Ni5Mo2Cu上位锁支臂开裂。通过现场调查、对断裂件的材料成分分析、金相组织观察、断口的宏微观观察、硬度检测以及设计结构、受力及现行工艺等综合分析,以确定该上位锁支臂断裂的性质及产生原因。结果表明：上位锁支臂的断裂为过大的装配应力、校形残余应力与氢共同作用下的氢致脆断造成的。此案例分析中发现了隔板设计结构、校形的残余应力问题,为此提出了合理的改进建议。