简介:采用一种新型高通量实验方法,实现对Ti-5553合金(Ti-5Al-5Mo-5V-3Cr,质量分数,%)在600~700℃范围内的连续温度梯度热处理。实验通过对圆台形样品进行直流电加热,由于截面面积不同而导致电流热效应不同,从而使样品表面温度呈梯度变化。采用端淬实验实现Ti-5553合金的连续冷却速率变化,研究合金在不同热处理条件下的显微组织演变和力学性能。结果表明:Ti-5553合金的伪调幅分解温度为(617±1)℃,析出的α相尺寸在300nm左右;合金在伪调幅分解温度下时效4h达到最高的硬度。因此,这种高通量方法能够快速准确地判断合金中相转变温度以及相应的组织转变。
简介:灼伤抵抗的钛合金的开发是在喷气引擎减轻钛火的点火和繁殖的最直接的方法。WSTi3515S合金(Ti-35V-15Cr-0.3Si-0.1C)是一种新高alloying贝它类型灼伤抵抗的钛合金,属于在在过去设计技术被使进步重要的Ti-V-Cr类型合金5?年。象有弹性的性质那样的WSTi3515S灼伤抵抗的钛合金的物理性质和热性质处于不同条件被测量并且分析。结果两个都显示出那幼仔模量并且砍WSTi3515S合金减少的模量稍微变化,温度在测试温度增加。WSTi3515S合金的泊松比率在0.36附近。然而,象特定的热,热扩散性,热传导性和热扩大那样的热性质增加,温度增加,它源于在提高的温度加强格子热颤动。并且WSTi3515S合金的房间温度密度是5.295?g????????????敮睴牯晫牯??
简介:Therulessuchasprocessparametersaffectingjointpropertiesandtheevolutionprincipleofweld'smicrostructurehavebeenresearchedbyadoptingdiffusionweldingprocesstoconnectSiCw/6061Alcomposite.ExperimentalresultsshowthatthereexistsacriticaltemperatureregionbetweensolidandliquidphaselineofSiCw/6061Alcomposite,andtheregionwillshrinkwiththeincreasingofweldingpressure.Whendiffusionweldingoccurredunderthecriticaltemperatureregion,weldingjointexhibitsbadpropertyofbonding,andthematrixandthereinforcementcan'tbondeffectively.Whendiffusionweldingoccurredinthecriticaltemperatureregion,thestrengthofweldingjointchangeswidelywiththevariationofweldingtemperature.Whenweldingtemperaturevariesin10℃,thestrengthofweldingjointwillchangeobviously.Onlywhenweldingtemperatureishigherthanthecriticaltemperatureregion,stablejointpropertiescanbeobtained.Simultaneouslythematrixandthereinforcementhasbetterinterfacialbondedindiffusionweldinginterface,andnoobviousinterfacereactionoccurred,andthusdiffusionweldingofSiCw/6061Alcompositecanbesuccessfullyrealized.
简介:采用扫描电镜、能谱仪以及X射线衍射仪对具有WC+β(β为钴基粘结相)两相结构的WC-11Co-0.71Cr3C2-0.06RE(RE为含La、Ce、Pr、Nd的混合稀土)硬质合金烧结体表面进行观察与分析。结果表明,在烧结过程中合金中的La、Ce、Pr、Nd通过定向迁移与烧结炉内气氛中的S、O等杂质元素结合,在合金烧结体表面形成RE2S3(主)和RE2O2S(少量)弥散相。从合金中Cr3C2的热力学稳定性、Cr在Co中的溶解度特性以及稀土原子激发等3个方面,对稀土迁移活性的激发机制和稀土原子的定向迁移机制进行分析与讨论。
简介:Theeffectofnonmetallicinclusionsinthedropletofthestainlesssteelcoveredelectrodeontheporositywasresearched.Theresultshowsthatthenonmetallicinclusionsinthedropletarespherical,theircompositionisdifferentfromtheoneofslagandtheinclusionshavethecharacterof"innerformation".Whentheratioofrutiletoilmeniteinthecoatedmaterialisincreased,thedropletbecomescoarse,thecontentofnonmetallicinclusioninthedropletdecreases,andtheporositysensitivityintheweldmetalalsodecreases.Whentheratiooffledspartoilmeniteinthecoatedmaterialisincreased,thedropletbecomesfine,thecontentofnonmetallicinclusioninthedropletincreases,andtheporositysensitivityintheweldmetalincreases.WhentheratioofFe2O3toilmeniteinthecoatedmaterialisincreased,thedropletbecomesfine,thecontentofnonmetallicinclusiondecreases,whiletheporositysensitivitydoesnotreduce.
简介:ThestoredenergyandtheenergyreleaseduringSPD(superplasticdeformation)ofaZn-5Alalloywerestudied.Thealloyafterrollingprocessgainsmorestoredenergy,andtheas-rolledspecimencanobtainmaximumelongationandminimumflowstresswithouthotholdingtreatmentbeforeSPD.ExperimentalresultsshowthatstoredenergyreleaseprocessisalongwithSPDprocessandisalsoanimpetustoSPD.Theas-rolledZn-5Alalloyhas48J/molstoredenergywhichwasmeasuredwithDSC(differentialscanningcalorimeter)andconformswelltothecalculatedvalue.Theas-rolledZn-5AlalloyafterSPDwithanelongationof2500%releases112J/molstoredenergy.Analysisshowsthatthestrainrateisindirectratiototherateofstoredenergyrelease.
简介:WeldingresearchofA6N01S-T5aluminumalloyprofileforhigh-speedtrainwasdonebyusinglaser-MIGhybridweldingandMIGweldingindividually.Andtheweldappearance,weldingdistortion,mechanicalpropertiesofthejointsandmicrostructureswereanalyzed.Thetestresultsdemonstratedthathigh-efficientweldingfortheprofilecanbeachievedbyusinglaser-MIGhybridwelding,thespeedofwhichcanbeover3.0m/min.Theprocessinghadagoodgapbridgingability,evenifthegapofthebuttjointwasupto2.0mm,agoodweldappearancecanalsobegot.Whilethehybridweldingspeedwasgreaterthan2.5m/min,theweldingdistortionofthelaser-tandemMIGhybridjointswasjustabout33%ofthatoftheMIGjoints,buttheweldingefficiencywasover3timesofMIGwelding.Andtensilestrengthofthehybridjointswas85%ofthatofA6N01S-T5basemetal,9%higherthanthatoftheMIGjoints.Fatiguepropertieswastestedindividuallywithpulsedtensilefatiguemethodintheconditionof1×107lifetime.Thetestresultsdemonstratedthatthefatiguestrengthofthejointswasalittlelowerthanthatofbasematerial,whichcouldbeupto115MPa.Butthefatiguestrengthofhybridweldingjointswas107.5MPa,whichwas23%higherthan87MPaofMIGweldingjoints.