简介：Aseriesofrhodium-modifiedMo-K/Al2O3catalystsampleswaspreparedbyvaryingtherhodiumloadingbetween0and1.0wt%andmaintainingmolybdenumandpotassiumcontentsasconstants.ThestructuresofthesampleswerecharaterizedbytechniquesofXRD.LRS.TPR,XPSandEXAFSandcorrelatedtothecatalyticpropertiesofthesamplesforalcoholsynthesisfromsynthesisgas,Itwasfoundthat.intheoxidicrhodium-modifiedsamples.astronginteractionoftherhodiummodifierwiththesupportedK-Mo-Ospeciesoccurs.Thisinteractionfacilitatesthesulfidationandreductionofthesupportedoxo-molybdenumandleadstoadecreaseinthesizeofthemolybdenumspeciesandstabilizationofthecationicrhodiumspeciesonthesamplesduringsulfidation.Uponsulfidation.Thesulfidedmolybdenumspeciesintherhodium-freesampleismanlypresentaslargepatechesofMoS2-likeslabswiththeirbasalsulfurplanesinteractingwiththesupportsurface.Withthemodiricationofrhodiumtothesamples.ThesupportedMoS2-likespeciesbecomeshighlydispersed.asrevealedbythedecreaseintheaveragesizeofthesulfidedmolybdenumspecies.TheinteractionoftherhodiumspecieswiththemolybdenumsomponentmaycausethebasalplanesoftheMoS2-likespeciestobecomeorientedperpendiculartothesupportsurfaceduetofavorablebondingoftheMoS2edgeplanestothesupportthroughMo-O-Albonds.Incomparisonwiththesulfidedsamplefreeofrhodium.thepropertiesoftherhodium-modifiedsamplesforalcoholsynthesisfromsynthesisgasaremuchimproved.Itmostprobablyresultsfromthesynergicinteractionoftherhodiumwiththemolybdenumspeciesthatgivesrisetotheappearanceofthecatalyticallyactivesurfacesofsites.Theco-existenceofcationicandmetallicrhodiumstabilizedbythisinteractionmayberesponsiblefortheincreasedselectivityfortheformationofC2+alcohols.

简介：

简介：

简介：

简介：Zn_(1-x)Cu_xOthinfilmsweresynthesizedbytheradiofrequency(RF)magnetronsputteringtechniqueusingaZnOtargetcontainingdifferentpiecesofsmallCu-chips.X-raydiffraction(XRD)andscanningelectronmicroscopy(SEM)wereemployedtoanalyzethecrystallineandmicrostructureofthefihn,andX-rayphotoelectronspectroscopy(XPS)wasusedtoestablishthebondingcharacteristicsandoxidationstatesofcopperinsidetheZnOhost.Roomtemperature(RT)ferromagnetismwasobservedintheZn_(1-x)Cu_xOfilmsbyaQuantumDesignsuperconductingquantmninterferencedevice(SQUID)andthesaturationmagneticmomentofthefilmswasfoundtodecreasewiththeincreaseinCucontent.

简介：本文介绍了BSRF4W1B束线及XAFS实验站八五改造工程的目标，主要工作，及改进后该实验系统达到的各项主要技术指标及运行状态。

简介：Vacuumtreatmentandion-beambombardmentaretwomajorprocessesinthelowenergyion-beamimplantation.Toaccuratelystudythecontributionsofthesetwomajorfactorstothebioeffectsseparately,theM_1generationvariationofArabidopsisthalianawithion-beamimplantationandvacuumtreatmentwerecomparedthroughaseriesofkeyplantdevelopmentparametersincludingmorphologicalobservation,biochemicalassayandRAPD(randomamplifiedpolymorphicDNA)analysis.Theresultsshowedthation-beamimplantationhadobviouseffectonalmostalloftheseparameters,andthevacuumtreatmenthadsomeimpactsonseveralmorphologicalparameterssuchastheboltingtimeandthelengthoftheprimarystem.Takingtheresultstogether,theindicationisthatvacuumtreatmenthassomeslightcontributionstothebioeffectsofion-beamimplantationwhileion-beambombardmentitselfisthemajorcreatorofthebioeffects.

简介：采用等量共浸和分步浸制备Co-Pt/γ-Al2O3催化剂。PtL-Ⅲ边的EXAFS结果表明。在氧化态样品中，Pt主要以氯化物形式存在；而在还原态样品中，Pt以氯化物和金属Pt形式共存，共浸法制得的样品中Pt-Cl配位明显，而分步浸法制得的样品中金属Pt为主要存在形式。Co-K边的EXAFS结果表明，氧化态样品中Co主要以Co3O4的形式存在，经氢还原后，Co以高分散的零价钴形式存在。共浸法制得的样品中Pt和Co物种具有更高的分散度。

简介：利用金刚石压砧高压装置（DAC），对Ca3Mn2O7的粉末样品进行了高压能散X射线衍射实验。结果表明，由于岩盐层易被压缩，在压力作用下层状钙钛矿结构锰氧化物Ca3Mn2O7的结构不稳定。在0－35GPa压力范围内，Ca3Mo2O7晶体结构发生了两次相变。在1．3GPa左右，由原来的四方相变为正交相，在9．5GPa左右，又由正交相向新的四方相转变。

简介：

简介：Anewrectangularpulsetriggergeneratorhasbeendevelopedwhichcangeneratetwo10kVpulseswitharisetimelessthan1ns,ajitterof0.2nsandawidthofabout10nsand40ns,respectively.Thisgeneratorusestwopolymer-foilswitchesand25ohmBlumleintransmissionlinescomposedoftwo-parallelstandardcoaxialcablesdischargingintotwo50ohmoutputcables.Thepulsewidthandthedelaybetweentwopulsescanbeadjustedbychangingthelengthofthecables.

简介：

简介：用XPS和同步辐射技术研究了钙钛矿型氧化物La1-xSnxMnO3薄膜的电子结构。特别地，我们采用角分辨X－射线光电子谱技术（ARXPS），研究了薄膜表面最顶层原子种类和排列状况。结果表明，La1-xSnxMnO3薄膜的表面最顶层为MnO2原子平面。在此基础上，我们进一步在原子水平上探讨了薄膜的层状外延生长机理。

简介：

简介：用同步辐射角分辨偏上光电子谱对K／Ru(101^-0)表面上吸附的CO分子轨道的对称性测量发现：结合能在11.2eV的CO－4α1（4σ）分子轨道对s偏振光（在沿＜12^-10>的入射面）是禁戒的。结果表明由于K的强烈影响，CO的分子轨道重新排列（sp^2杂化）。根据选择定则和分子轨道的对称性说明，sp^2再杂化的CO分子吸附的桥位取向是<12^-10>晶向。

简介：

简介：目前，北京同步辐射装置4W1A束线的双晶单色器存在着调节困难、单色光出口不固定等问题，本文对其中原因进行了讨论，并提出一种新型结构的双晶单色器。此单色器具有调节简单、波长切换方便等优点，并实现了单色光固定出口。从而能够大大缩短调光时间，提高4W1A束线专用光的用光效率。

简介：

简介：本文对合成制备的LiNiO2、LiCo2和LiNixCo1-xO2正极材料以及稀土金属Ce元素添加改性的正极材料进行了XRD和EXAFS表征。结果表明，随着焙烧温度的升高，物相组成趋于单一，晶格趋向完整，800℃时完全形成LiNiO2、LiCoO2晶相结合。LiNiCoO2样品中Ni/Co比不影响LiNiO2晶相的形成，而只影响其晶相组成；掺杂的稀土金属Ce元素以CeO2状态存在于产物中，CeO2对LiNiO2晶相形成有一定的影响；LiCoO2的焙烧温度不能大于900℃，否则Co被氧化为Co3O4；样品中Ni与Co原子的局域结构，除Ni与Co原子相互影响外，掺杂Ce后对它们的局域结构也有较大影响。

简介：利用同步辐射（BSRF）漫散射站四圆衍射仪，对SiC体单晶的结构进行了判定以及对利用常压化学气相沉积（APCVD）生长的3C－SiC/Si(001）中的孪晶及含量进行了分析。六方{10-15}极图证明了该SiC单晶为6H（H为Hexagonal的缩写）结构。对3C－SiC外延薄膜，Φ扫描证明了3C－SiC外延生长于Si衬底上，外延取向关系为：（001）3C－SiC//(001)Si,[111]3C-SiC//[111]Si。3C－SiC的{111}极图在x=15.8°出现了新的衍射，采用六方{10-10}极图以及基体倒格点111、孪晶倒格点002的Mapping分析了x=15.8°处产生的衍射为3C－SiC孪晶所致，并利用ω扫描估算了孪晶的含量约为1％。