简介：包含Pechini方法和火花血浆sintering(SPS)方法的一条典型途径为高密度Li5+xSrxLa3xBi2O12的准备被介绍(x=0，1)陶艺。阶段形成，微观结构，谷物尺寸和标本的电的性质用XRD，SEM和交流电阻抗光谱学(酸)被检验。有纯像石榴石的阶段，97%的相对密度和大约5m的平均谷物尺寸的稠密的Li5La3Bi2O12和Li6SrLa2Bi2O12陶艺用这条途径被制作。在陶艺由SPS方法准备了的Li5La3Bi2O12和Li6SrLa2Bi2O12的298K的全部的传导性是5.1吗？？

简介：Withpositronannihilationradiationonedimensionangular-correlationdevice,itismeasuredthatpositronannihilationradiationonedimensionangular-correlationcurvesofpolycrystalsodiumionconductorNa5Y1-xCrxSi4O12（NYCS）system.Afterelectronmomentumdistributioncurvesarenormalized,linearparametersarecalculated.TheparametersH,WandSshowthechangeofNa+ionvacancyconcentrationinNYCSseriessamples.TheresultsshowthatparametersH,WandSofonedimensionangular-correlationcurvesofthosesamplesvarygreatlywithCr2O3contents.WithCr2O3contentincreasing,HandSparametersincrease,butWdecreases,andreachesextremesatx=0.05;thenwithCr203addingcontinually,parametersHandSdecreasegradually,parameterWincreasesgradually.Thisshowsthat,inaddtiontoCr2O3,theconductivityhascloserelation

简介：

简介：以1-氯-1-苯乙烷（1-PECl）为引发剂、CuCl／N，N，N’，N＂，N＂-五甲基二乙撑三胺（PMDETA）为催化体系，采用原子转移自由基聚合法制备大分子引发剂PtBMA—C1和PtBMA-b-PNIPAM，两亲性嵌段共聚物PtBMA-b-PNIPAM在选择性溶剂中自组装成胶束。采用红外和核磁共振谱表征了PtBMA-b-PNIPAM嵌段共聚物的结构及组成，采用GPC得到了其相对分子质量，并且采用动态光散射和透射电镜分别研究了自组装得到的胶束的温敏性和形态。

简介：铁磁性微晶玻璃由于具有磁性和生物活性，可以用作磁感应热疗的热种子材料。采用SiO2-Na2O-CaO-P2O5-Fe2O3五元系统，通过共沉淀-熔融法和熔融法两种不同的方法制备铁磁性微晶玻璃，利用XRD确定其晶相并计算晶体的晶格常数和晶粒尺寸，并通过VSM表征样品的磁性能。结果表明，玻璃液在自然冷却的过程中就形成了大量的磁铁矿，不经过热处理过程即可制得具有磁铁矿唯一晶相的铁磁性微晶玻璃并具有生物活性。共沉淀-熔融法制备的样品磁性更强。

简介：以超重力场辅助燃烧合成技术制备了呈梯度分布的Y2O3-Al2O3-SiO2玻璃／Y3Al5O12陶瓷梯度复合材料。结果表明，梯度布置两种组分的原料既可防止下层熔体的喷溅，又能提高上层玻璃的透过率。该梯度材料沿超重力方向依次为YAS透明玻璃层、YAS-YAG玻璃陶瓷层和YAG陶瓷层。

简介：用固相反应法制备了LnBaCo2O5＋δ（Ln=Gd，Nd，Sm，Pr）-Ba0．5Sr0．5Co0．8Fe0．2O3-δ（质量比为1：1）4种双相混合导体膜。通过XRD分析可知，除了PrBaCo2O5＋δ和Ba0．5Sr0．5Co0．8Fe0．2O3-δ（KSCF）复合时发生明显反应外，其它3种复合膜在复合过程中均显示了良好的化学兼容性。4种双相膜在850℃时透氧率最高的是NdBa-Co2O5＋δ-Ba0．5Sr0．5Co0．8Fe0．2O3-δ（约为0．28mL／（cm2·min））。